Chapter 13      Wrought Stainless Steels

 [ Back  ] [ Home ] [ Up ] [ Table of Contents ] [ Next ]

 MECHANICAL PROPERTIES OF WROUGHT PRECIPITATION-HARDENING STAINLESS STEELS

130f

ASTM

Heat Treat

Tensile Strength

Yield Strength

 

 

Hardness
125f

Specification

Conditionm

ksi

MPa

ksi

MPa

% El

% RA

HRCk
180g                  
 (UNS S13800)                  
 B, F A 564, A 705 H950 220 1520 205 1410 10 45; 35b 45
 B, F A 564, A 705 H1000 205 1410 190 1310 10 50; 40b 43
 B, F A 564, A 705 H1025 185 1275 175 1210 11 50; 45b 41
 B, F A 564, A 705 H1050 175 1210 165 1140 12 50; 45b 40
 B, F A 564, A 705 H1100 150 1030 135 930 14 50 34
 B, F A 564, A 705 H1150 135 930 90 620 14 50 30
 B, F A 564, A 705 H1150M 125 860 85 585 16 55 26
 P, Sh, St A 693 H950 220 1520 205 1410 6-10c --- 45
 P, Sh, St A 693 H1000 200 1380 190 1310 6-10c --- 43
 15-5 PH                  
 (UNS S15500)                  
 B, F A 564, A 705 H900 190 1310 170 1170 10; 6b 35; 15b 40
 B, F A 564, A 705 H925 170 1170 155 1070 10; 7b 38; 20b 38
 B, F A 564, A 705 H1025 155 1070 145 1000 12; 8b 45; 27b 35
 B, F A 564, A 705 H1075 145 1000 125 860 13; 9b 45; 28b 32
 B, F A 564, A 705 H1100 140 965 115 795 14; 10b 45; 29b 31
 B, F A 564, A 705 H1150 135 930 105 725 16; 11b 50; 30b 28
 B, F A 564, A 705 H1150M 115 795 75 515 18; 14b 55; 35b 24
 P, Sh, St A 693 H900 190 1310 170 1170 5-10c --- 40-48
 P, Sh, St A 693 H1100 140 965 115 790 5-14c --- 29-40
Product ASTM Heat Treat Tensile Strength Yield Strength     Hardness
Forma Specification Conditionm ksi MPa ksi MPa % El % RA HRCk
 PH 15-7 Mo                  
 (UNS S15700)                  
 B, F A 564, A 705 RH950 200 1380 170 1210 7 25 ---
 B, F A 564, A 705 TH1050 180 1240 160 1100 8 25 ---
 P, Sh, St A 693 A 150 max 1035 max 65 max 450j 25 min --- ---
 P, Sh, St A 693 RH950d 225 1550 200 1380 1-4c --- 45-46*
 P, Sh, St A 693 TH1050d 190 1310 170 1170 2-5c --- 40
 P, Sh, St A 693 CR cond C 200 1380 175 1210 1 41 ---
 P, Sh, St A 693 CH900 240 1650 230 1590 1 --- 46
 17-4 PH                  
 (UNS 17400)                  
 B, F A 564, A 705 H900d 190 1310 170 1170 10 40; 35e 40
 B, F A 564, A 705 H925d 170 1170 155 1070 10 44; 38e 38
 B, F A 564, A 705 RH950d 155 1070 145 1000 12 45 35
 B, F A 564, A 705 H1025d 145 1000 125 860 13 45 32
 B, F A 564, A 705 H1075d 140 965 115 795 14 45 31
 B, F A 564, A 705 H1100d 135 930 105 725 16 50 28
 B, F A 564, A 705 H1150Md 115 795 75 515 18 55 24
 P, Sh, St A 693 H900 190 1310 170 1170 5-10c --- 40-48
 P, Sh, St A 693 H1100 140 965 115 790 5-14c --- 29-40
 AM-350                  
 (UNS S35000)                  
 P, Sh, St A 693 A 200 max 1380 max 85-90 585- 8-12c --- 30l
          maxc 620c,j      
 P, Sh, St A 693 H850 185 1275 150 1030 2-8c --- 42
 P, Sh, St A 693 H1000 165 1140 145 1000 2-8c --- 36
Product ASTM Heat Treat Tensile Strength Yield Strength     Hardness
Forma Specification Conditionm ksi MPa ksi MPa % El % RA HRCk
 AM-355                  
 (UNS S35500)                  
 F A 705 H1000 170 1170 155 1070 12 25 37
 P, Sh, St A 693 H850 190 1310 165 1140 10 --- ---
 P, Sh, St A 693 H1000 170 1170 150 1030 12 --- 37
 Custom 450                  
 (UNS S450000)                  
 B, Shapes A 564f A 130f 895f 95 655 10 40 32l
 F, Shapes A 705f A 125f 860f 95 655 10 40 33l
 B, F, Shapes A 564g, A 705g H900 180g 1240g 170 1170 6; 10b 20; 40b 39
 B, F, Shapes A 564g, A 705g H950 170g 1170g 160 1100 7; 10b 22; 40b 37
 B, F, Shapes A 564g, A 705 H1000 160g 1100g 150 1030 8; 12b 27; 45b 36
 B, F, Shapes A 564g, A 705 H1025 150g 1030g 140 965 12 45 34
 B, F, Shapes A 564g, A 705 H1050 145g 1000g 135 930 9; 12b 30; 45b 34
 B, F, Shapes A 564g, A 705 H1100 130g 895g 105 725 11; 16b 30; 50b 30
 B, F, Shapes A 564g, A 705 H1150 125g 860g 75 515 12-18h 35-55h 26
 P, Sh, St A 693 A 130-165 895-1205 90-150 620-1035 4 min --- 25-33
 P, Sh, St A 693 H900 180 1240 170 1170 3-5c --- 40
 P, Sh, St A 693 H1100 160 1105 150 1035 5-7c --- 36
 P, Sh, St A 693 H1150 125 860 75 515 8-10c --- 26
Product ASTM Heat Treat Tensile Strength Yield Strength     Hardness
Forma Specification Conditionm ksi MPa ksi MPa % El % RA HRCk
 Custom 455                  
 (UNS S45500)                  
 B, F, Shapes A 564g, A 705g H900i 235 1620 220 1520 8 30 47
 B, F, Shapes A 564g, A 705g H950i 220 1520 205 1410 10 40 44
 B, F, Shapes A 564g, A 705g H1000i 205 1410 185 1280 10 40 40
 P, Sh, St A 693 H950 222 1530 205 1410 4 max --- 44
 a. B - bar; F - forging; P - plate; Sh - sheet; St - strip; W - wire.
 b. Higher value is longitudinal; lower value is transverse.
 c. Values vary with thickness or diameter.
 d. Longitudinal properties only.
 e. Higher values are for sizes up to and including 3 in. (75 mm); lower values are for sizes over 3 in. (75 mm) up to and including 8 in. (200 mm).
 f. Tensile strength of 125 to 165 ksi (860 to 1140 MPa) for sizes up to 0.50 in.(13 mm).
 g. Tensile strength only applicable up to sizes of 0.50 in. (13 mm).
 h. Varies with section size and test direction.
 i. Up to and including 6 in. (151 mm).
 j. Maximum value.
 k. Single hardness values are maximums, unless otherwise specified; hardness values identified as ranges are minimum-maximum, except
 PH 15-7 A 693 - RH950 hardness range 45-46* is a minimum value. 
 l. Hardness value is a maximum.
 m. A - annealed; CR - cold rolled; CD - cold drawn.
 
 [ Go to Top ]
 

 The Ferrous Metals Data Book